A team of researchers with members from Lawrence Livermore National Laboratory, Wright-Patterson Air Force Base and the Barnes Group Advisors found that controlling spatter during laser-powder bed fusion can reduce defects in metal-based 3-D printing. In their paper published in the journal Science, the group describes studying the additive manufacturing printing methodology and what they learned about it. Andrew Polonsky and Tresa Pollock with the University of California, Santa Barbara have published a Perspective piece on the work done by the team in the same journal issue.
As additive manufacturing printing methodologies mature, new materials are being tested to find out if they might be used in 3-D printers to create new products. In recent years, this has extended to metals. One such technique is called laser-powder bed fusion (L-PBF). It involves the use of a high-powered laser to melt and fuse metallic powders layer by layer to produce a 3-D part. It has been hoped that the technique could eventually be used for aerospace and biomedical applications. But thus far, such efforts have fallen short due to the large number of defects that occur with the process. In this new effort, the researchers have discovered a way to reduce such defects, perhaps paving the way for the technique to finally fulfill its promise.
To better understand why the L-PBF process leads to so many defects (such as undesired pores) the researchers conducted X-ray synchrotron experiments and built predictive multi-physics models to gain a better understanding of what occurs during printing. One of their goals was to better understand how energy is absorbed during printing with powder layers that are only a few particles thick.
The researchers found that a large number of the defects were the result of simple spatter—material expelled from the process interfering with recently forged material. Further study revealed that much of the spatter that was produced during the process could be mitigated by carefully controlling the laser power as it was applied. They found that doing so greatly reduced the number of defects in the objects that were produced.
Saad A. Khairallah et al. Controlling interdependent meso-nanosecond dynamics and defect generation in metal 3D printing, Science (2020). DOI: 10.1126/science.aay7830
© 2020 Science X Network
Controlling spatter during laser powder bed fusion found to reduce defects in metal-based 3-D printing (2020, May 18)
retrieved 18 May 2020
This document is subject to copyright. Apart from any fair dealing for the purpose of private study or research, no
part may be reproduced without the written permission. The content is provided for information purposes only.